UV Resistant Urethane Resin
ECU-UVR
ECU-UVR is a two-component, 90% solids, VOC compliant, polyurethane coating that was developed as a topcoat. The product contains a UV protector. It provides a glossy finish with superior chemical resistance. It exhibits excellent physical properties. This system has been approved by the Canadian Food Inspection Agency (CFIA).
$600.003 Gallon Kit
Documents
Primary Applications
- Marine protection for fiberglass, steel, concrete or wood
- UV-stable top coat
- Aircraft hangar floors
- Low temperature equipment
- Maintenance facilities
- Industrial shop floors
- Car washes or wash bays
- Secondary containment
- Cooling towers
- Bridges
- Wastewater treatment applications
Advantages
- Long pot life (30 min to 40 min)
- Displays fast cure times in thin film
- Respectable odor
- Superior chemical resistance (compared to standard epoxy)
- Abrasion resistant
- Non yellowing and good gloss retention
- Dense surface resistant to bacteria and humidity
- Excellent adhesive properties, allowing application on other firm and hard coating, as well as a good bond to the substrate
- VOC complaint in Canada and the United States
Technical Data
| Packaging litres / gal us | Color | |||||
|---|---|---|---|---|---|---|
| 11.34 / 3 | 56.7 / 15 | Part A | Part B | Mixture | ||
| Recommended Thickness | Light Yellow | Clear | Light Yellow | |||
| Primer: ECE | 8 mils / 200 ft² us gal | Shelf Life | ||||
| Topcoat on solid color: ECU-UVR | 6-8 mils / 200-265 ft² us gal | |||||
| Topcoat on vinyl flakes: ECU-UVR | 8 – 12mils / 133-200 ft² us gal | 12 months in original unopened factory sealed containers. Keep away from extreme cold, heat, or moisture. Keep out of direct sunlight and away from fire hazards. | ||||
| Mix Ratio by volume | ||||||
| A : B = 2 : 1 | ||||||
| *Please note that the indicated mileage is calculated for flat surfaces. A porous or imperfect surface will require more material in order to cover the same mileage. | ||||||
| Pot life (150g) | Solids by weight % | Density (kg/litre) | ||||
| 25-30 minutes 25°C | 90.6 | Part A | Part B | Mixture | ||
| VOC (g/litre) | Recommended Thinner | 1.06-1.08 | 1.15-1.17 | 1.09-1.10 | ||
| 33.7 | xylene | Solids by weight % | ||||
| Viscosity @ 25⁰C (cps) | Part A | Part B | Mixture | Part A | Part B | Mixture |
| 400-500 | 1750-3250 | 1100-1200 | 85.5 | 100 | 90.6 | |
| Waiting time between coats | ||||||
| Min / 6-10 hours – max / 24 hours | ||||||
| Foot Traffic | 12 – 24 hours | |||||
| Light Traffic | 48 hours | |||||
| Chemical Resistance | 72 hours | |||||
| *Note: Times and data mentioned are based on laboratory conditions. Field results may vary and will be affected by changing ambient conditions, especially changes in temperature and relative humidity. | ||||||